Design and Construction from Local Materials of an Aluminum Recycling Foundry
Downloads
In the low-carbon global aluminum cycle actual perspective, the need of remelting aluminum is in constant increase. The objective of this work was to build a portable aluminum foundry based on local materials. This foundry can be used to make small spare parts in complete safety and/or as practical melting equipment. The foundry is made up of a butane combustion Furnace and various tools for handling molten aluminum. The Furnace was manufactured by recycling a defective gas cylinder. After removing the top of the bottle, we lined the inside with a layer of local clay which serves as a 5-centimeter thermal insulator. The crucible was made by recycling a waste hermetic compressor, and the tools by recycling scrap metal. The tests carried out allowed to melt used cans and other parts of motorbikes and cars defective in aluminum. Liquid aluminum was cast to obtain cylindrical and prismatic blanks for machining, as well as other small mechanical parts. The cost of carrying out the project has been estimated at nearly 150,000 XAF.
R. Ammour et D. Ikerrouiene, « Etude et Conception d’un moule d’injection d’alliage d’aluminium pour un flasque-bride d’un moteur électrique B5-A106/107-2 », PhD Thesis, Université Mouloud Mammeri Tizi-Ouzou, 2017.
J. Corbion, « Le savoir… fer », Gloss. Haut Fourn. Assoc. Savoir… Fer Serémange, 2016.
H. Haddadi et A. Gana, « Etude et conception d’un moule d’injection aluminium pour la production d’une patte de carcasse type163 », PhD Thesis, Université Mouloud Mammeri Tizi Ouzou, 2022.
C. Cullen, J. M., Jonathan M. et Allwood. (s. d.) J. M. ,. Jonathan M. et Allwood. (s. d. ). et C. Cullen, J. M., Jonathan M. et Allwood. (s. d.) J. M. ,. Jonathan M. et Allwood. (s. d. )., « Cartographie du flux mondial d’aluminium : De l’aluminium liquide aux produits d’utilisation finale. Science de l’environnement & technologie, 47, 3057‑3064. », 2021.
R. Mensi, P. Acker, et A. Attolou, « Séchage du béton: analyse et modélisation », Mater. Struct., vol. 21, p. 3‑12, 1988.
Menzie, G., WD et Barry, JJ et Bleiwas, DI et Bray, EL et Goonan, TG et Matos. (s. d.), « Le flux mondial d’aluminium de 2006 à 2025. US Department of the Interior, US Geological Survey. » 2006.
J. M. Cullen et J. M. Allwood, « Mapping the global flow of aluminum: from liquid aluminum to end-use goods », Environ. Sci. Technol., vol. 47, no 7, p. 3057‑3064, 2013.
M. Langhorst, R. G. Billy, C. Schwotzer, F. Kaiser, et D. B. Müller, « Inertia of Technology Stocks: A Technology-Explicit Model for the Transition toward a Low-Carbon Global Aluminum Cycle », Environ. Sci. Technol., 2024.
M. F. Audry, « La démarche d’analyse fonctionnelle », Académie Versailles, 2010.
B. de la Bretesche, La méthode APTE: Analyse de la valeur, analyse fonctionnelle. Ed. Pétrelle, 2000.
R. Tassinari, Pratique de l’analyse fonctionnelle. Dunod, 2006.
L. Zehtaban et D. Roller, « Systematic functional analysis methods for design retrieval and documentation », Int. J. Comput. Inf. Eng., vol. 6, no 12, p. 1711‑1716, 2012.